Polyamide hot melt adhesive and hemming adhesive DY-P403
|Acid Value,(mg KOH/g ≤)||5|
|Amine Value,(mg KOH/g≤)||3|
|Tensile Strength, (≥ MPa)||13|
|Water absorption, (≤ %)||0.4|
|Shear Strength, (≥ MPa, AL/AL)||10|
|Stretch Rate, (≥ %)||250|
|Operating Temperature( ºC )||190-200|
Yellowish round grain with schistose shape
This is a general type of polyamide hot-melt adhesive, which is
made from dimer acid and polyamine through condensation reaction at
It can dissolve in general organic solvents, the hot-melting
viscosity of the resin is greatly related to the temperature that
The polyamide hot-melt adhesive possesses the following advantages,
such as lower viscosity, good fluidity, good flexibility, high
adhesive strength, good media corrosion resistance, good solubility
and fluxing property at low temperature, higher heat stability etc.
This type of resin is applied in heat-shrinkable sleeve for
electric cable, sealing material for electrical connection,
cementing or fixing materials for electronic component, bonding
material for package, textile, leather, wood, plastic, metal and
Packaging and Storage:
Double packing: craft paper-plastic composite bag lined with PE
Net weight: 25Kgs per bag.
Storage: kept in cool, airy and dry place, keep the package sealed
before using up.
More appropriate price under the same quality as the one from our
Timely and effective service based on quality and technic.
Shorter lead time based on requirements from clients.