6168 Structural AB epoxy adhesive for wind blade , thixotropy Industrial strength glue

Categories AB Glue
Brand Name: HUIIAN
Model Number: 6169
Place of Origin: CHINA
MOQ: 400 KG
Price: USD 10.00/KG
Payment Terms: L/C, T/T
Supply Ability: 100 TONS MONTH
Delivery Time: 8-15 DAYS
Packaging Details: 200kg/ barrel
Appearance: B light blue thixotropic paste
Chemical Composition: B modified amine
Density 23℃(: B 1.28
weight ratio: A:B=100:50
Operation time (min, 23℃): 30 MIN
  • Product Details
  • Company Profile

6168 Structural AB epoxy adhesive for wind blade , thixotropy Industrial strength glue

6168 wind blade structural adhesive is a two component epoxy adhesive, high-thixotropic, light green, high toughness, high strength epoxy adhesive.

Typical use

GRP and FRP adhesive such as fan blade mold, yachts, sports equipment..

Characteristics before curing

Typical values range

A component

Appearance light yellow high thixotropic paste

Chemical Composition modified epoxy resin

Density 23℃(GB/T 15223-2008) 1.27

Viscosity (mPa.s) (GB/T 22314-2008) 470000

B component

Appearance light blue thixotropic paste

Chemical Composition modified amine

Density 23℃(GB/T 15223-2008) 1.20

Viscosity (mPa.s) (GB/T 22314-2008) 450000


Mixing characteristics

Appearance light green thixotropic paste

weight ratio A:B=100:50 A:B=100:52±2

Operation time (min, 23℃) 199

(DIN 16945-1989)

Curing time (h, 75℃)6

Characteristics after curing(23℃, 50%RH)

Shear strength (MPa,Al-Al) (GB/T 7124-2008)

3mm 24.6

0.5mm 31.1

Tensile strength (body, 23℃, MPa)58

(ISO 527-2:1993) 44

The tensile modulus (body, 23℃,GPa)

(ISO 527-2:1993) 4.82

T- peel strength(N/mm, Al-Al)(GB/T 1692-2008)

3mm 4.42

0.5mm 2.86

distortion temperature(℃) 69

(ISO 75-2-2004)

glass transition temperature(℃) 75.4

(ISO 11357-2-1997)


flow(5℃-40℃): 5cmLift not sag


Use Instructions

Surface preparation: It can be directly used for non-porous surface. Porous or absorbent surface should be mixed with a resin liquid filled pores after class.

Mixing: mix with weight ratio of A:B=100:50, the

increase or decrease outside the allowance in the

amount of curing agent will accelerate or reduce the

rate of curing, leading to incompletely curing. This

can not be modified again. A and B must be mixed

very evenly, until no turbidity is visible. Yellow A andblue B can be visually recognized. Special attention should be paid to the bottom and wall of the mixing vessel. It is very difficult to mix a lot of glue by hand because of the high viscosity. Mixing equipment is necessary to ensure a larger amount of glue for

industrial use.

Curing: Mixed plastic should be at 20-30 ℃, the surface temperature of the adhesive material should be controlled not more than 35 ℃. Before curing, remove the excess glue from the surface sticky. The curing process, the components should be heated slowly so that the internal stress of the adherend to a minimum. Thick layer (greater than 10mm) colloidal curing, need to consider a phased temperature curing in order to control the impact of concentrated heat. Temperature test center by layer, helping to set procedures to improve production efficiency and performance of the adhesive.

Security

Please refer to the MSDS for detailed safety Information.

Package

Order code: Shanghai

A 6168 200kg/ barrel, 2 barrels / box.

B 6168 200kg/ barrel, 2 barrels / box.

Storage

Stored in a cool, dry place at 8-28℃ for 24 months
.

Quality 6168 Structural AB epoxy adhesive for wind blade , thixotropy Industrial strength glue for sale
Send your message to this supplier
 
From:
Enter your email please.
To: Shanghai Huitian New Material Co., Ltd
Subject:
Message:
Characters Remaining: (0/3000)
 
You may also be interested in :
Inquiry Cart 0
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    Contact Us Quickly