Categories | Hardness Tester |
---|---|
Place of Origin: | Beijing |
Brand Name: | SADT |
Certification: | ISO9001 |
Model Number: | W-20 |
MOQ: | 1pc |
Packaging Details: | Standard package |
Delivery Time: | Within one week after receiving payment |
Payment Terms: | T/T in advance |
Supply Ability: | 50pcs/week |
Price: | USD400-700/Pcs |
Testing Range: | 0~20HW |
Accuracy: | 0.5HW |
Weight: | 0.5kg |
Applicable Materials: | Aluminum alloy |
Sample requirement: | thickness 0.6 mm - 6 mm inner diameter >10 mm |
Standards: | ASTM B647-84(2000), YS/T420-2004, JJG944-2013 |
Warranty: | 1 year |
Certificate: | ISO9001 SGS |
Aluminium Alloy Portable Hardness Tester ASTM B647 Standard With High Accuracy
Features:
A portable instrument which can perform on-site hardness test on
soft metals in accordance with American Standard ASTM B647.
Used to check the result of heat treatment and determine if the mechanical performace of the workpiece is acceptable.
Suitable for testing the hardness of aluminium profiles, tubings, sheets and other shapes.
Used for testing the with long or heavy workpieces or assemblies inconvenient to be sent to the labs.
Ideal for qualification inspection on the production site.
Used to test aluminum profiles.
Application
W-20 Webster hardness tester is used to test aluminum profiles on the production site and application. It is used to test the aluminum alloy tubings with inner diameter more than 10mm
Operating Method
Put the specimen between the anvil and the indenter and press down
the handle until the bottom is felt. At the time the dial indicator
will point at a reading which is the hardness value obtained.
Excessive pressure beyond this limit can not damage the tester, but
it’s unnecessary. Hold tight the handle when reading the value. Any
torsion or move will make the reading incorrect during the test.
Models Selection:
Item | Type | Applicable Materials | Hardness Range | Specimen Size/ mm |
1 | W-20 | Aluminum alloy | 25-110 HRE 58-131 HV | Thickness 0.4-6 Inner diameter>10 |
2 | W-20a | Thickness 0.4-13 Inner diameter>10 | ||
3 | W-20b | Thickness 0.4-8 Inner diameter>6 | ||
4 | B75 | Brass in hard or half hard state, super-hard aluminum alloy | 63-105 HRF | Thickness 0.4-6 Inner diameter>10 |
5 | B75-2 | Thickness 0.4-8 Inner diameter>6 | ||
6 | BB75 | Soft brass, pure copper | 18-100 HRE | Thickness 0.4-6 Inner diameter>10 |
7 | BB75-2 | Thickness 0.4-8 Inner diameter>6 | ||
8 | B92 | Cold-rolled steel sheet, stainless steel | 50-92 HRB | Thickness 0.4-6 Inner diameter>10 |
![]() |